THERMAL BEHAVIOUR OF γ-IRRADIATED NYLON 610

JIN Yan; CHEN Donglin

Your Location：

Home >

Browse articles >

THERMAL BEHAVIOUR OF γ-IRRADIATED NYLON 610

Papers | Updated：2021-06-21

- THERMAL BEHAVIOUR OF γ-IRRADIATED NYLON 610
- Vol. 6, Issue 3, Pages: 216-222(1988)
- Affiliations：
- Author bio：
- Funds：
- DOI：
  CLC：
- Published：20 September 1988
- Accepted：
Scan QR Code
JIN Yan, CHEN Donglin. THERMAL BEHAVIOUR OF γ-IRRADIATED NYLON 610[J]. 1988, 6(3): 216-222.
DOI：

JIN Yan, CHEN Donglin. THERMAL BEHAVIOUR OF γ-IRRADIATED NYLON 610[J]. 1988, 6(3): 216-222. DOI：

摘要

The thermal behaviour of γ-irradiated nylon 610 was investigated. In DSC (differential scanning calorimetry) thermograms in addition to general features characteristic of γ-irradiatinn cross-linked crystalline polymers

a typical cold-crystallization phenomenon was observed during the sceond scan for samples that had been subjected to high radiation dose. G-values for cresslinking nylon 610 were estimated from gel fraction measurement and TMA (thermomechanical analysis)

From TMA curves it was estimated that the dimensional stability of properly irradiated nylon 610 articles might be raised up to ca.300℃。

Abstract

From TMA curves it was estimated that the dimensional stability of properly irradiated nylon 610 articles might be raised up to ca.300℃。

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

One-handed Helical Poly(m-terphenyl acetylene)s with Broad Optical Activity Range from Ultraviolet-Visible to Near-infrared Regions

Preparation and Chiral Recognition Ability of Crystalline Cellulose Phenylcarbamate

Advances in Polymer-based Circularly Polarized Luminescent Materials

Sliding Dynamics of Ring Chain on a Rod-Coil Block Copolymer in Rotaxane

Multiple-Responsive Chiral Hydrogels from Helical Dendronized Poly(phenylacetylene)s

Related Author

No data

Related Institution

No data

⁰