CRYSTALLIZATION AND MULTI-MELTING BEHAVIOR OF POLY (ETHYLENE TEREPHTHALATE) MODIFIED BY SODIUM SALT OF 5-SULPHO-ISOPHTHALIC ACID

Papers | Updated：2021-06-21

- CRYSTALLIZATION AND MULTI-MELTING BEHAVIOR OF POLY (ETHYLENE TEREPHTHALATE) MODIFIED BY SODIUM SALT OF 5-SULPHO-ISOPHTHALIC ACID
- Vol. 5, Issue 1, Pages: 53-60(1987)
- Affiliations：
- Author bio：
- Funds：
- DOI：
  CLC：
- Published：20 March 1987
- Accepted：
Scan QR Code
HU Hengliang, MU Xiangqi, WU Shizhen. CRYSTALLIZATION AND MULTI-MELTING BEHAVIOR OF POLY (ETHYLENE TEREPHTHALATE) MODIFIED BY SODIUM SALT OF 5-SULPHO-ISOPHTHALIC ACID[J]. 1987, 5(1): 53-60.
DOI：

HU Hengliang, MU Xiangqi, WU Shizhen. CRYSTALLIZATION AND MULTI-MELTING BEHAVIOR OF POLY (ETHYLENE TEREPHTHALATE) MODIFIED BY SODIUM SALT OF 5-SULPHO-ISOPHTHALIC ACID[J]. 1987, 5(1): 53-60. DOI：

摘要

The crystallization kinetics of the copolyester

poly(ethylene terephthalate) (PET) modified by sodium salt of 5-sulpho-isophthalic acid(SIPM)

was investigated by means of differential scanning calorimeter. The experimental results and polari-microscopy observation all showed that the introduction of SIPM did not affect the nucleation of crystallization. Within the temperature range between their glass transition temperature Tθ and melting point Tm

the crystallization rate of the copolyester sample decrrased with increasing content of SIPM.The relative crystallization rate constant Z of SIPM/DMT (dimethyl terephthalate)4mol% sample was about 1% pure PET's Z value.For isothermal crystallized copolyester samples

DSC heating curves displayed multi-melting behavior.This was interpreted by molecalar weight fractionation during crystallization and premelting-recrystallization mechanism.This interpretation showed why the second melting point Tm2 will change according to Hoffman-Weeks(H-W) equation[1] and the first melting point Tm1 will increase with increasing SIPM.The principal cause of these phenomena is the high temperature crystallization rate decreases rapidly with increasing SIPM.

Abstract

The crystallization kinetics of the copolyester

poly(ethylene terephthalate) (PET) modified by sodium salt of 5-sulpho-isophthalic acid(SIPM)

关键词

Keywords

references

Views

Downloads

CSCD

Alert me when the article has been cited

Submit

Tools

Publicity Resources

Manipulating Hierarchical Aggregation Structure via Film-forming Kinetics Enables Organic Photovoltaics over 20% Efficiency

Advances in Polymer-based Circularly Polarized Luminescent Materials

Molecular Segregation and Melt Memory in Dilute Polycaprolactone with Reduced Entanglements

Topology-regulated Co-assembly of Single Chain Polymer Nanoparticles and Block Copolymers into Hierarchical Micelle@Vesicle Composite Structures

Optically Active Helical Poly(phenyl isocyanide)s Bearing Achiral Benzanilide Pendants: from Controlled Synthesis to Enantioseparation Application

Related Author

No data

Related Institution

No data

⁰